Dezhou Supply of epoxy intermediate coat of iron, the paint, lacquers transition WB-842 epoxy micaceous iron oxide intermediate lacquer, epoxy resin, polyamide resin, gray micaceous iron oxide, thickeners and other components two component rust. The main characteristics of the zinc-rich primer has and steel with zinc layer excellent adhesion and sealing properties with good adhesion on galvanized steel appropriately treated with excellent adhesion on sandblasted steel can be used for atmospheric and underwater steel facilities for industrial and chemical atmosphere has good weather resistance with good abrasion resistance and, after the film has good interlayer adhesion. Both with two cans of epoxy, polyurethane and chlorinated rubber-based paint and other facilities, also with alkyd, phenolic and other traditional type of paint were supporting the film for a long time to maintain a good impact resistance and flexibility use of excellent durability can be used as epoxy zinc primer, inorganic zinc primer and other high performance anticorrosive intermediate layer paint, in order to enhance the protection of the performance of the coating; it can be used as the iron and steel metal sprayed zinc coating or plating Closed zinc coating steel surfaces; also be directly anti-rust primer coating of the steel surface by sandblasting. Color and Appearance: gray, dull. Basic parameters: a density of about 136g / cm3 (mixed) dry film thickness of 50 ~ 100um wet film thickness of 110 ~ 120um theoretical amount 150 ~ 300g / m2 Flash Point Part A (base material) 27 ° C and Part B (Curing Agent) 27 ° C Drying time (25 ° C) ≤ 2h hard work table dry completely cured ≤ 24h 7d recoat time Substrate temperature 5 ° C 20 ° C 30 ° C Shortest 48h 24h 16h Part A ratio of up to three months : B = 45: 1 (by weight) (To add a diluent, can be added after the A, B groups were mixed) Curing time (20 ° C) 30min applicable period (20 ° C) 8h proposal Tu loaded word count: airless spray together, brush or roller two to three, about a film thickness of 100um. Front-matching paint: WB-702 epoxy low zinc shop primer (or direct-coated on the steel surface rust quality reaches the level Sa25) After matching paint: epoxy paint, chlorinated rubber paint, alkyd paint, polyurethane paint, epoxy asphalt rust, paint and other phenolic. Finish: steel coated with zinc primer: In addition to the net all the oil, debris and zinc galvanized steel: the elastic grinding wheel in addition to net all the oil, debris and zinc with; as for underwater parts of the It must swipe sandblasted surface treatment. Steel: Blast cleaning to Sa25 level. Shopprimed steel: sand blasting or pneumatic tools using a second swipe rust, rust quality of St3. Airless spray coating method: H06 thinner Diluting Thinner 0-10% (by weight paint) nozzle diameter of about 0.4 ~ 05mm discharge pressure 20-25MPa (about 200-250kg / cm2) air spraying: thinner H06 diluent amount of 0-10% (by weight paint) nozzle diameter of about 1.5 ~ 2.0mm air pressure 03 ~ 0.4MPa (3 ~ 6kg / cm2) Roller / Brush: Thinner H06 thinner Diluting: O- 5% (by weight paint) Cleaner: H06 Thinner Packaging: Group A (base) 20L barrels 18kg Group B (curing agent) 4L barrels 4.Okg shelf life: 12 months Dezhou supply ring intermediate coat of iron oxide, in the paint, lacquers transition WB-842